Zirconium Silicate Beads, ZrSiO4, is obtained from imported zircon sand, and formed by sintering phasing method, offering superior toughness and high compressive strength and low wear loss.

These Zirconium Silicate Beads are less dense than yttria-stabilized zirconia spheres, suitable for calcium carbonate, Kaolin, Tianium dioxide, paitings, coatings, ink and pesticides, etc..

Chemical composition	ZrO2>65%
Chemical composition	SiO2 <35%
True Density	4.0g/cm3
Bulk density	2.5g/cm³
Wear rate per ton	0.03kg/h
Moh's hardness	8
Color	Milky white
Package	25kg/ barrel

Size (Diameter/mm) :

0.1-0.2	0.2-0.3	0.3-0.4	0.5-0.6
0.6-0.8	0.8-1.0	1.0-1.2	1.0-1.2
1.4-1.6	1.6-1.8	1.8-2.0	2.0-2.2
2.2-2.4	2.4-2.8	2.8-3.2	4,5,6,7,8,9,10

Good sphericity-Low abrasion loss, long life time. Wearability is 8-10 times higher than glass beads;
High Density-High Grinding efficiency. Grinding efficiency is 3-5 times higher than glass beads;
High crushing strength, reduce the intermal friction between the beads and improve the material flow efficiency
Good icid and alkali-resistance and good chemical stability

Printing Inks
Pigments / Dyes
Painting&Coatings
Calcium carbobate/Kaolin
Pesticide suspension

Horizontal sand Mill
Vertical Sand Mill
Vertical Attrition Mill
High Speed Ultra Fine Sand Mill
Basket Mill